Zirconia Powder 1050MPa Dental Material Block For CAD CAM Milling

Shenzhen Xiangtong Co.,Ltd.

Zirconia Powder 1050MPa Dental Material Block For CAD CAM Milling

Brand Name : XTCERA

Model Number : TT

Certification : CE, FDA, ISO

Place of Origin : China

MOQ : 50

Price : Negotiable

Payment Terms : T/T, Western Union

Supply Ability : 1500pcs/day

Delivery Time : 10working days

Packaging Details : Box Package

Name : dental zirconia blank

Vickers Hardness : 1250HV

Chemical Solubility : <100μg/m²

ZrO2+HfO2 : >90wt%

Y2O3 : 4.5-9.5wt%

Type : Denture Material

Contact Now

Natural Color Transition,No Need Dyeing

zirconia blocksare made of nanometer medical grade zirconia powder. The powder are firstly compacted by cold isostaticpressing with high compressive strength and then pre-sintered to a certain degree to offer good machinability.

Us zirconia blocks can be used to create crowns, bridges, inlays and veneers of fixed partial denture with different translucency levels and colors.

Layer Proportion

Vickers

Hardness(HV)

Strength(MPa) Color Translucency
Layer 1 30% ≥1250 ≥1050

Shallow

Deep

49%
Layer 2 15%
Layer 3 15%
Layer 4 20%
Layer 5 20%

Available in all classic VITA 16 shades (A1 to D4)

Indications For Use
XTCERA SHT Multilayer is intended for the fabrication and preparation of copings, full
anatomical/ full contour crowns, bridges up to three uints, inlays, and onlays for anterior and
posterior restorations.
Note:Directing arrow is marked on the label of multilayer blanks, which points to insical surface.

Chemical Composition

Component Content
ZrO2+HfO2 >90wt%
Y2O3 4.5-9.5wt%
AL2O3 <0.5wt%
Other Oxides <0.2wt%

Properties

Projects Detection result
Sintering Density ≥6.0g/cm³
Bending Strength ≥1050MPa
Vickers Hardness 1250HV
Chemical Solubility <100μg/m²

Operation Guide

1). Place zirconia block in your CAD/CAM machine and machine it following the manufacturer’s instructions.

2). After machining is completed, remove the zirconia block from the CAD/CAM machine first. Then remove the framework from the zirconia block with a diamond disc. Subsequently, place the framework on a sintering tray with zirconia beads and put them in the oven for sintering.

3). Program the furnace according to its instruction manual and zirconia block’s sintering chart, and then start sintering.

4). Do not remove the sintered framework until it is fully cooled down. Examine the sintered framework for wall thickness, margin fit and seat fit. If necessary, make minor adjustments with a water cooled diamond tool.

5). Make sure no wall thickness is less than 0.5mm and no connector is thinner than 9mm2.

6). Rinse the sintered framework with water and dry completely. The framework

XTCEAR was founded in 2001,owning 20 years' R&D experience on Zirconium Dioxide
Ceramic Material and Industrial CNC Milling Machine.
As a member of Aviation Industry of China(AVIC), XTCERA has 1400 employees and over
30,000 square meters R&D and production base.
In the past 10 years, XTCERA has sold out about 4000 units dental milling machines and
supplied over 1,000,000 pieces of dental Zirconia blanks per year in the global dental market.
We believe quality is the life of product and trust is the foundation of business relation.
Zirconia Powder 1050MPa Dental Material Block For CAD CAM Milling

Product Tags:

1050MPa Dental Material Block

      

Zirconia Powder Dental Material Block

      

CAD CAM Milling Zirconia Blocks

      
Wholesale Zirconia Powder 1050MPa Dental Material Block For CAD CAM Milling from china suppliers

Zirconia Powder 1050MPa Dental Material Block For CAD CAM Milling Images

Inquiry Cart 0
Send your message to this supplier
 
*From:
*To: Shenzhen Xiangtong Co.,Ltd.
*Subject:
*Message:
Characters Remaining: (0/3000)